Edge adhesive viscosity and can not directly reflect the performance of plastic
good or bad. Under normal circumstances, the higher the viscosity of the edge 
 sealing adhesive, the better the initial adhesive strength,but the worse the 
coatin but the worse the coating performance. Low-viscosity hot-melt
glue smaller amount of wetting better. Some high viscosity hot melt adhesive
curing, it's also possible to have a high initial strength.

For poor quality particleboard, edge sealing need to use high viscosity hot
melt adhesive, which is because the high viscosity of the hot melt adhesive
is poor, when the glue is not as low viscosity hot melt adhesive into the
edge of the chipboard easy to enter the pores , So that the hot melt adhesive
can be fully coated in the edge of the plate
.
 

Related News
Read More >>
What are the characteristics of environmentally friendly edge sealing hot melt adhesives? What are the characteristics of environmentally friendly edge sealing hot melt adhesives?
Oct .20.2022
The solid content is 100%, and it has void filling properties, which avoids the defects such as deformation, dislocation and shrinkage of the adhered parts caused by edge curling, air bubbles and cracking.
Appearance And Prospect Of Edge Sealing Hot Melt Adhesive Appearance And Prospect Of Edge Sealing Hot Melt Adhesive
Sep .22.2022
Environmentally friendly edge sealing hot melt adhesive is a green and pollution-free environmental friendly adhesive.
What kinds of situations often occur when hot melt adhesive particles are used in furniture edge sealing? What kinds of situations often occur when hot melt adhesive particles are used in furniture edge sealing?
Aug .26.2022
1. Black edge phenomenon: The hot melt machine has not been cleaned for a long time, and the glue itself has carbonization phenomenon.
Reasons for the open edge of the edge band Reasons for the open edge of the edge band
Aug .13.2022
The moisture content of the edge banding wood is unqualified (>18%), and the natural drying during the use of the door leaf produces internal stress, resulting in cracking and deformation of the edge banding.